Ratnashri Metals is a leading Supplier, Manufacturer & Exporter of Stainless Steel 904L (UNS N08904) Sheet, Stainless Steel 904L Plates, Stainless Steel 904L Coils, Stainless Steel 904L Seamless Pipes, Stainless Steel 904L Railing Pipes, Stainless Steel 904L Welded & ERW pipes & tubes.

Stainless Steel 904L is stocked by 23 North American distributors and produced by 28 large mills. Distributors will offer small quantity buys while mills will generally only sell large quantities, with delivery times anywhere from 10 to 50 weeks depending on size and form required This material is stocked primarily in Flat Rolled Products by 10 distributors but is also available to a lesser extent in Tubular Products, Wire Products, Piping Components, Bar Products, and Structurals.

Specifications

The following specifications cover Stainless Steel 904L

AFNOR Z2CNDU 25-20

ASTM B625

ASTM B649

ASTM B673

ASTM B674

ASTM B677

DIN 1.4539

UNS N08904

Property Results
Related Metals:

VLX904(tm)

AL 904L(tm)

Cronifer 1925 LC(tm)

In what form is Stainless Steel 904l available at Ratnashri Metals?

Bar

Wire

Sheet

Plate

Forgings

Pipe

Flanges

Chemistry Data

Chemical Composition ranges of 440C stainless steel

Principal Design Features

904L is an austenitic stainless steel designed for moderate to high corrosion resistance. Its low carbon content improves cleanliness and weld strength.

Applications

Utility scrubber assemblies, acid and fertilizer production equipment.

Machinability

Slow speeds and positive feeds will minimize this alloy's tendency to work harden and glaze. Use chip breakers where possible to overcome problems with long draggy chips.

Welding

Most common fusion and resistance methods may be employed. For maximum corrosion resistance, it is recommended to use filler metals of equal or higher alloy content.

Hot Working

Hot work should proceed after uniform heating to 2000-2200 F. Doe not work the material at less than 1800 F. Full annealing should follow any hot work to reattain maximum ductility and corrosion resistance.

Cold Working

Although higher forces are required, 904L will respond in a similar fashion to other austenitic stainless steels like 304, 316 or 317. Most common operations can be successfully performed.

Annealing

1920-1990 F (1050-1090 C), rapid cooling.

Hardening

This alloy does not respond to heat treatment.. It may only be hardened by cold reduction.

Physical Data

Density (lb / cu. in.)	0.285
Specific Gravity	7.9
Specific Heat (Btu/lb/Deg F - [32-212 Deg F])	0.12
Electrical Resistivity (microhm-cm (at 68 Deg F))	480
Modulus of Elasticity Tension	28.4

Mechanical Data

Form	Sheet
Condition	Test Specimen Annealed
Temper	70
Tensile Strength	87
Yield Strength	40
Elongation	50
Reduction of Area	55
Rockwell	B79