Lean Duplex S32304


Duplex-S31803 sheets plates round bars pipes tubes

Ratnashri Metals is a leading Supplier, Manufacturer & Exporter of Lean Duplex S32304 (UNS S32304) Sheet, Lean Duplex S32304 Plates, Lean Duplex S32304 Coils, Lean Duplex S32304 Seamless Pipes, Lean Duplex S32304 Railing Pipes, Lean Duplex S32304 Welded & ERW pipes & tubes.

The alloy lean duplex 2304 has similar corrosion resistance properties to 316L. Furthermore, its mechanical properties i.e. yield strength, are twice those of 304/316 austenitic grades. This allows the designer to save weight, particularly for properly designed pressure vessel applications.


Chemical Analysis

TYPICAL VALUES (WEIGHT %)

C

CR

NI

MO

N

OTHERS

0.020

23

4

0.2

0.1

S = 0.001

PREN (‰Cr+3.3‰Mo+16‰N) ≥ 24

Mechanical Properties

TENSILE PROPERTIES (MINIMUM VALUES)

°C

RP 0.2
MPA

RP 1.0
MPA

RM
MPA

°F

YS 0.2‰
KSI

YS 1.0‰
KSI

UTS
KSI

ELONGATION
‰

20

400

440

600

68

58

64

87

25

100

330

365

570

212

48

53

83

25

200

280

310

530

392

41

45

77

20

30

230

260

490

572

33

38

71

20

DENSITY: 7,800 KG/ – 0.28 LB/IN3

INTERVAL
TEMPER
°C

THERMAL
EXPANSION
ΑX10-6K-1

°C

RESISTIVITY
(ΜΩ CM)

THERMAL
CONDUCTIVITY
(W.M-1.K-1)

SPECIFI
HEAT
(J.KG-1.K-1)

YOUNG
MODULUS
E
(GPA)

SHEAR
MODULUS
G
(GPA)

20-100

13

20

80

17

450

200

75

100

92

18

500

190

73

20-200

13.5

200

100

19

530

160

70

20-300

14

300

105

20

560

170

67

In what form is Lean Duplex S32304 available at Ratnashri Metals?
  • Bar
  • Wire
  • Sheet
  • Plate
  • Forgings
  • Pipe
  • Flanges

    • Send us a enquiry

    Thanks for sending your message! We'll get back to you shortly.

    There was a problem sending your message. Please try again.

    Please complete all the fields in the form before sending.

    Contact Info

    • 22/3, Vannier Street,
      Chennai - 600 001.
    • +91-94440 48983
    • ratnashrimetals@yahoo.co.in
    OUR SUMMARY:
    Review Date
    Reviewed Item
    Lean Duplex S32304 sheets plates round bars pipes tubes
    Author Rating
    5