Ratnashri Metals is a leading Supplier, Manufacturer & Exporter of Inconel Alloy X-750 (UNS: N07750) Sheet,Inconel Alloy X-750 Plates, Inconel Alloy X-750 Coils, Inconel Alloy X-750 Seamless Pipes, Inconel Alloy X-750 Railing Pipes, Inconel Alloy X-750 Welded & ERW pipes & tubes.
Alloy X-750 is a precipitation-hardenable alloy which has been used in applications such as high temperature structural members for gas turbines, jet engine parts, nuclear power plant applications, heat-treating fixtures, forming tools, and extrusion dies. The alloy is highly resistant to chemical corrosion and oxidation and has high stress-rupture strength and low creep rates under high stresses at temperatures up to 1500°F (816°C) after suitable heat treatment.
X750 is a Nickel-Chromium alloy made precipitation hardenable by additions of Al and Ti, having creep-rupture strength at high temperatures to about 700oC (1290oF). It is widely used for high temperature conditions but is not as strong as Nimonic 90.
Alloy X-750 is a precipitation-hardenable alloy which has been used in applications such as high temperature structural members for gas turbines, jet engine parts, nuclear power plant applications, heat-treating fixtures, forming tools, and extrusion dies. The alloy is highly resistant to chemical corrosion and oxidation and has high stress-rupture strength and low creep rates under high stresses at temperatures up to 1500°F (816°C) after suitable heat treatment.
Element |
Min |
Max |
Carbon |
-- |
0.08 |
Manganese |
-- |
0.30 |
Silicon |
-- |
0.50 |
Sulfur |
-- |
0.01 |
Nickel + Cobalt |
70.0 min |
|
Chromium |
14.0 |
17.0 |
Iron |
5.00 |
9.00 |
Aluminum |
0.40 |
1.00 |
Titanium |
2.25 |
2.70 |
Copper |
-- |
0.50 |
Cb + Ta |
0.70 |
1.20 |
Density
lb/cu in...................................... 0.300
kg/cu m...................................... 8303
Melting Range
°F........................................ 2540/2600
°C.........................................1393/1427
Temperature |
Btu-in/ft²-hr-°F |
W/m-K |
|
°F |
°C |
||
300 |
149 |
117 |
16.9 |
Condition |
ohm-cir mil/ft |
microhm-mm |
At Room Temperature |
||
Hot Rolled |
764 |
1270 |
Temperature |
psi x 10(6) |
MPa x 10(6) |
|
°F |
°C |
||
80 |
26.7 |
31.0 |
213.7 |
Room Temperature Mechanical Properties.
Temper |
Tensile Strength, |
Yield Strength |
Elongation |
Hardness, |
Hot-finished + 1300°F/20 hr,A.C |
170,000-206,000 |
120,000-163,000 |
25-15 |
313-400 |